- 缺口冲击强度: 28.0
- 弯曲模量 [MPa]: 17.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Linear Mold Shrinkage, Flow | 0.00 cm/cm | 0.00 in/in | ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 140 MPa | 20300 psi | 5mm/min; ISO 527-2/1A | ||
| Elongation at Break | 1.2 % | 1.2 % | 5mm/min; ISO 527-2/1A | ||
| 1.8 % | 1.8 % | flexural; ISO 178 | |||
| Tensile Modulus | 17.0 GPa | 2470 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 200 MPa | 29000 psi | ISO 178 | ||
| Flexural Modulus | 17.0 GPa | 2470 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 28.0 kJ/m² | 13.3 ft-lb/in² | ISO 180/1A | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 335 °C | 635 °F | ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 270 °C | 518 °F | ISO 75-1, -2 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 30.0 °C | 68.0 - 86.0 °F | hopper | ||
| 80.0 - 120 °C | 176 - 248 °F | cavity | |||
| Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |||
| Zone 1 | 315 - 325 °C | 599 - 617 °F | |||
| Zone 2 | 320 - 330 °C | 608 - 626 °F | |||
| Zone 3 | 325 - 335 °C | 617 - 635 °F | |||
| Zone 4 | 330 - 340 °C | 626 - 644 °F | |||
| Die Temperature | 335 - 345 °C | 635 - 653 °F | |||
| Melt Temperature | 335 - 345 °C | 635 - 653 °F | |||
| Drying Temperature | 150 - 170 °C | 302 - 338 °F | |||
| Dry Time | 4 - 6 hour | 4 - 6 hour | |||
| Moisture Content | 0.010 % | 0.010 % | Necessary low maximum | ||
| Injection Pressure | 50.0 - 150.0 MPa | 7250 - 21750 psi | |||
| Hold Pressure | 50.0 - 150.0 MPa | 7250 - 21750 psi | |||
| Back Pressure | <= 3.00 MPa | <= 435 psi | |||
| Screw Speed | 80 rpm @Diameter 40.0 mm | 80 rpm @Diameter 1.57 in | |||
| 140 rpm @Diameter 25.0 mm | 140 rpm @Diameter 0.984 in | ||||
| 200 rpm @Diameter 16.0 mm | 200 rpm @Diameter 0.630 in | ||||
| Hot-Working Temperature | 335 - 345 °C | 635 - 653 °F | |||
| Descriptive Properties | |||||
| Injection speed | very fast | ||||
| Remarks | When using short metering strokes an accumulator is recommended to get short injection times. | ||||