- 缺口冲击强度: 0.747
- 弯曲强度 [MPa]: 135.0
- 弯曲模量 [MPa]: 16.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.63 g/cc | 1.63 g/cc | ASTM D792 |
| Water Absorption | <= 0.010 % | <= 0.010 % | 24 hours; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.00070 cm/cm | 0.00070 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0038 cm/cm | 0.0038 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 135 MPa | 19600 psi | ASTM D638 |
| Elongation at Break | 1.3 % | 1.3 % | ASTM D638 |
| Tensile Modulus | 15.9 GPa | 2300 ksi | ASTM D638 |
| Flexural Strength | 184 MPa | 26700 psi | ASTM D570 |
| Flexural Modulus | 16.2 GPa | 2350 ksi | ASTM D570 |
| Izod Impact, Notched | 0.747 J/cm | 1.40 ft-lb/in | ASTM D256 |
| Izod Impact Unnotched | 8.13 J | 6.00 ft-lb | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.00e+17 ohm-cm | 2.00e+17 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | ASTM D257 |
| Dielectric Constant | 4.2 @Frequency 100 Hz | 4.2 @Frequency 100 Hz | ASTM D150 |
| Dielectric Strength | 35.4 kV/mm @Thickness 1.60 mm | 900 kV/in @Thickness 0.0630 in | ASTM D149 |
| Dissipation Factor | 0.0106 @Frequency 100 Hz | 0.0106 @Frequency 100 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | -0.900 µm/m-°C @Temperature 20.0 °C | -0.500 µin/in-°F @Temperature 68.0 °F | Flow Direction; ASTM E831 |
| CTE, linear, Transverse to Flow | 54.0 µm/m-°C @Temperature 20.0 °C | 30.0 µin/in-°F @Temperature 68.0 °F | ASTM E831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 298 °C | 568 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 3.17 mm | V-0 @Thickness 0.125 in | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 321 - 360 °C | 610 - 680 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Drying Temperature | 149 °C | 300 °F | |
| Dry Time | 6 - 8 hour | 6 - 8 hour | |
| Dew Point | -28.9 °C | -20.0 °F | |