- 密度 [g/cm3]: 1.0
- 吸水率 [%]: 0.1
- 缺口冲击强度: 0.2
- 拉伸强度 [MPa]: 30.0
- 断裂伸长率 [%]: 70.0
- 弯曲强度 [MPa]: 48.0
- 弯曲模量 [MPa]: 6.60
- 热变形温度 [℃]: 200.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.00 - 2.20 g/cc | 0.0361 - 0.0795 lb/in³ | Average value: 1.76 g/cc Grade Count:69 |
| Apparent Bulk Density | 0.600 - 1.15 g/cc | 0.0217 - 0.0415 lb/in³ | Average value: 0.869 g/cc Grade Count:14 |
| Water Absorption | 0.100 - 0.500 % | 0.100 - 0.500 % | Average value: 0.183 % Grade Count:19 |
| 0.150 - 0.900 % @Temperature 50.0 - 50.0 °C | 0.150 - 0.900 % @Temperature 122 - 122 °F | Average value: 0.244 % Grade Count:14 | |
| 0.150 - 0.900 % @Time 173000 - 173000 sec | 0.150 - 0.900 % @Time 48.0 - 48.0 hour | Average value: 0.244 % Grade Count:14 | |
| Viscosity | 325 - 1300 cP | 325 - 1300 cP | Average value: 816 cP Grade Count:9 |
| Linear Mold Shrinkage | 0.00100 - 0.00600 cm/cm | 0.00100 - 0.00600 in/in | Average value: 0.00282 cm/cm Grade Count:33 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Barcol | 63.0 - 73.0 | 63.0 - 73.0 | Average value: 70.2 Grade Count:9 |
| Hardness, Rockwell M | 98.0 - 105 | 98.0 - 105 | Average value: 103 Grade Count:3 |
| Hardness, Shore D | 85.0 - 89.0 | 85.0 - 89.0 | Average value: 87.6 Grade Count:9 |
| Tensile Strength, Ultimate | 48.0 - 550 MPa | 6960 - 79800 psi | Average value: 183 MPa Grade Count:54 |
| Tensile Strength, Yield | 30.0 - 80.0 MPa | 4350 - 11600 psi | Average value: 58.1 MPa Grade Count:8 |
| Elongation at Break | 0.600 - 2.04 % | 0.600 - 2.04 % | Average value: 1.57 % Grade Count:15 |
| Modulus of Elasticity | 6.00 - 30.0 GPa | 870 - 4350 ksi | Average value: 16.4 GPa Grade Count:29 |
| Flexural Yield Strength | 70.0 - 1200 MPa | 10200 - 174000 psi | Average value: 269 MPa Grade Count:65 |
| >= 160 MPa @Temperature 150 - 150 °C | >= 23200 psi @Temperature 302 - 302 °F | Average value: 166 MPa Grade Count:5 | |
| Flexural Modulus | 6.60 - 35.0 GPa | 957 - 5080 ksi | Average value: 18.0 GPa Grade Count:52 |
| Compressive Yield Strength | 120 - 1000 MPa | 17400 - 145000 psi | Average value: 295 MPa Grade Count:55 |
| Compressive Modulus | 7.60 - 16.7 GPa | 1100 - 2420 ksi | Average value: 10.7 GPa Grade Count:5 |
| Shear Strength | 20.0 - 74.0 MPa | 2900 - 10700 psi | Average value: 39.9 MPa Grade Count:15 |
| Izod Impact, Notched | 0.200 - 24.0 J/cm | 0.375 - 45.0 ft-lb/in | Average value: 3.02 J/cm Grade Count:24 |
| Izod Impact, Notched (ISO) | 60.0 - 80.0 kJ/m² | 28.6 - 38.1 ft-lb/in² | Average value: 66.7 kJ/m² Grade Count:6 |
| Izod Impact, Unnotched (ISO) | 34.0 - 54.0 kJ/m² | 16.2 - 25.7 ft-lb/in² | Average value: 45.1 kJ/m² Grade Count:9 |
| Charpy Impact Unnotched | 0.400 - 6.00 J/cm² | 1.90 - 28.6 ft-lb/in² | Average value: 2.66 J/cm² Grade Count:20 |
| Charpy Impact, Notched | 0.150 - 0.800 J/cm² | 0.714 - 3.81 ft-lb/in² | Average value: 0.406 J/cm² Grade Count:9 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 - 1.00e+16 ohm-cm | 1.00e+12 - 1.00e+16 ohm-cm | Average value: 2.61e+15 ohm-cm Grade Count:10 |
| Surface Resistance | 1.00e+13 - 1.00e+15 ohm | 1.00e+13 - 1.00e+15 ohm | Average value: 5.78e+14 ohm Grade Count:13 |
| Insulation Resistance | 5.00e+7 - 5.00e+11 ohm | 5.00e+7 - 5.00e+11 ohm | Average value: 1.47e+11 ohm Grade Count:20 |
| Dielectric Constant | 1.80 - 7.00 | 1.80 - 7.00 | Average value: 4.88 Grade Count:47 |
| Dielectric Strength | 0.984 - 40.0 kV/mm | 25.0 - 1020 kV/in | Average value: 14.7 kV/mm Grade Count:39 |
| Dielectric Breakdown | >= 35000 V @Temperature 90.0 - 90.0 °C | >= 35000 V @Temperature 194 - 194 °F | Average value: 32900 V Grade Count:9 |
| >= 10000 V @Temperature 90.0 - 90.0 °C | >= 10000 V @Temperature 194 - 194 °F | Average value: 32900 V Grade Count:5 | |
| >= 10000 V @Time 20.0 - 60.0 sec | >= 10000 V @Time 0.00556 - 0.0167 hour | Average value: 32900 V Grade Count:5 | |
| Dissipation Factor | 0.00500 - 0.0500 | 0.00500 - 0.0500 | Average value: 0.0244 Grade Count:47 |
| Arc Resistance | 120 - 190 sec | 120 - 190 sec | Average value: 168 sec Grade Count:22 |
| Comparative Tracking Index | 180 - 600 V | 180 - 600 V | Average value: 281 V Grade Count:26 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 3.60 - 47.0 µm/m-°C | 2.00 - 26.1 µin/in-°F | Average value: 24.7 µm/m-°C Grade Count:19 |
| 10.0 - 77.4 µm/m-°C @Temperature 37.8 - 150 °C | 5.56 - 43.0 µin/in-°F @Temperature 100 - 302 °F | Average value: 36.9 µm/m-°C Grade Count:9 | |
| Thermal Conductivity | 0.277 - 0.800 W/m-K | 1.92 - 5.55 BTU-in/hr-ft²-°F | Average value: 0.546 W/m-K Grade Count:14 |
| Maximum Service Temperature, Air | 130 - 240 °C | 266 - 464 °F | Average value: 150 °C Grade Count:7 |
| Maximum Service Temperature, Inert | 140 - 200 °C | 284 - 392 °F | Average value: 168 °C Grade Count:6 |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | Average value: 200 °C Grade Count:4 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 - 282 °C | 230 - 540 °F | Average value: 239 °C Grade Count:33 |
| Deflection Temperature at 8.0 MPa | 100 - 200 °C | 212 - 392 °F | Average value: 162 °C Grade Count:9 |
| Glass Transition Temp, Tg | 60.0 - 170 °C | 140 - 338 °F | Average value: 97.6 °C Grade Count:12 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:22 |
| Oxygen Index | 33.5 - 50.0 % | 33.5 - 50.0 % | Average value: 42.9 % Grade Count:4 |
| Shrinkage | 0.000 - 0.150 % | 0.000 - 0.150 % | Average value: 0.0483 % Grade Count:6 |
| <= 0.0500 % @Temperature 110 - 110 °C | <= 0.0500 % @Temperature 230 - 230 °F | Average value: 0.0500 % Grade Count:6 | |
| <= 0.0500 % @Time 605000 - 605000 sec | <= 0.0500 % @Time 168 - 168 hour | Average value: 0.0500 % Grade Count:6 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 150 - 175 °C | 302 - 347 °F | Average value: 163 °C Grade Count:3 |
| Melt Temperature | 40.0 - 110 °C | 104 - 230 °F | Average value: 76.5 °C Grade Count:5 |
| Mold Temperature | 143 - 190 °C | 289 - 374 °F | Average value: 172 °C Grade Count:9 |
| Pot Life | 20.0 - 120 min | 20.0 - 120 min | Average value: 92.2 min Grade Count:9 |
| Shelf Life | 6.00 Month | 6.00 Month | Average value: 6.00 Month Grade Count:6 |