  4. Overview of materials for Epoxy Cure Resin

Overview of materials for Epoxy Cure Resin

Overview of materials for Epoxy Cure Resin 物性表: Overview of materials for Epoxy Cure Resin物性表及特性介绍,Overview of materials for Epoxy Cure Resin注塑参数详情,如需Overview of materials for Epoxy Cure Resin下载, 可到相关下载区下载
  • 密度 [g/cm3]: 0.86
  • 吸水率 [%]: 0.03
  • 拉伸强度 [MPa]: 1.03
  • 断裂伸长率 [%]: 92.0
  • 弯曲强度 [MPa]: 5.17
  • 弯曲模量 [MPa]: 0.00350
  • 透光率 [%]: 90.0
 
Physical PropertiesMetricEnglishComments
Density 0.860 - 2.60 g/cc0.0311 - 0.0939 lb/in³Average value: 1.33 g/cc Grade Count:103
 1.025 - 1.06 g/cc
@Temperature 15.0 - 15.0 °C		0.03703 - 0.0383 lb/in³
@Temperature 59.0 - 59.0 °F		Average value: 1.05 g/cc Grade Count:3
Solids Content 59.0 - 100 %59.0 - 100 %Average value: 78.2 % Grade Count:20
Volatiles 5.00e-7 - 3.92 %5.00e-7 - 3.92 %Average value: 0.355 % Grade Count:34
Water Absorption 0.0300 - 1.00 %0.0300 - 1.00 %Average value: 0.298 % Grade Count:25
Moisture Absorption at Equilibrium 2.80 - 9.40 %2.80 - 9.40 %Average value: 5.16 % Grade Count:7
Viscosity 0.650 - 1.20e+6 cP0.650 - 1.20e+6 cPAverage value: 36500 cP Grade Count:102
 15.0 - 78000 cP
@Temperature 40.0 - 156 °C		15.0 - 78000 cP
@Temperature 104 - 313 °F		Average value: 8950 cP Grade Count:4
Molecular Weight 158 - 1690 g/mol158 - 1690 g/molAverage value: 661 g/mol Grade Count:11
Linear Mold Shrinkage 0.00100 - 0.00400 cm/cm0.00100 - 0.00400 in/inAverage value: 0.00240 cm/cm Grade Count:5
Vapor Pressure 2.10e-8 - 0.0100 bar0.0000158 - 7.50 torrAverage value: 0.00250 bar Grade Count:4
 0.0100 - 0.0100 bar
@Temperature 50.0 - 50.0 °C		7.50 - 7.50 torr
@Temperature 122 - 122 °F		Average value: 0.00400 bar Grade Count:3
Storage Temperature 23.0 - 25.0 °C73.4 - 77.0 °FAverage value: 23.5 °C Grade Count:4
 
Mechanical PropertiesMetricEnglishComments
Hardness, Shore D 50.0 - 95.050.0 - 95.0Average value: 80.4 Grade Count:27
Tensile Strength, Ultimate 5.17 - 97.0 MPa750 - 14100 psiAverage value: 33.7 MPa Grade Count:31
 35.8527 - 35.8527 MPa
@Temperature 149 - 149 °C		5200.01 - 5200.01 psi
@Temperature 300 - 300 °F		Average value: 35.9 MPa Grade Count:1
Tensile Strength, Yield 1.03 - 2900 MPa150 - 420000 psiAverage value: 576 MPa Grade Count:102
 4.137 - 2571.74 MPa
@Temperature -55.0 - 190 °C		600.0 - 373001 psi
@Temperature -67.0 - 374 °F		Average value: 626 MPa Grade Count:17
Elongation at Break 0.000 - 50.0 %0.000 - 50.0 %Average value: 9.35 % Grade Count:33
 2.40 - 6.90 %
@Temperature 75.0 - 300 °C		2.40 - 6.90 %
@Temperature 167 - 572 °F		Average value: 4.65 % Grade Count:1
Elongation at Yield 1.00 - 13.0 %1.00 - 13.0 %Average value: 3.49 % Grade Count:30
Modulus of Elasticity 0.00370 - 215 GPa0.537 - 31200 ksiAverage value: 35.9 GPa Grade Count:99
 1.572 - 164.095 GPa
@Temperature -67.0 - 220 °C		228.0 - 23800.4 ksi
@Temperature -88.6 - 428 °F		Average value: 57.7 GPa Grade Count:17
Flexural Yield Strength 92.0 - 1890 MPa13300 - 274000 psiAverage value: 921 MPa Grade Count:33
 108.937 - 1380.95 MPa
@Temperature 50.0 - 177 °C		15800.0 - 200290 psi
@Temperature 122 - 350 °F		Average value: 942 MPa Grade Count:7
Flexural Modulus 0.00350 - 205 GPa0.508 - 29700 ksiAverage value: 56.0 GPa Grade Count:34
 3.13711 - 109.075 GPa
@Temperature 50.0 - 177 °C		455.007 - 15820.2 ksi
@Temperature 122 - 350 °F		Average value: 63.0 GPa Grade Count:7
Compressive Yield Strength 2.76 - 1690 MPa400 - 246000 psiAverage value: 358 MPa Grade Count:79
 52.0 - 1585.79 MPa
@Temperature -55.0 - 177 °C		7540 - 230000 psi
@Temperature -67.0 - 351 °F		Average value: 574 MPa Grade Count:21
Compressive Modulus 0.0552 - 168 GPa8.00 - 24300 ksiAverage value: 45.2 GPa Grade Count:59
 12.0 - 162.027 GPa
@Temperature -55.0 - 177 °C		1740 - 23500.4 ksi
@Temperature -67.0 - 351 °F		Average value: 62.1 GPa Grade Count:16
Poissons Ratio 0.350 - 0.4200.350 - 0.420Average value: 0.389 Grade Count:10
Fracture Toughness 0.433 - 3.69 MPa-m½0.394 - 3.36 ksi-in½Average value: 1.33 MPa-m½ Grade Count:18
Shear Modulus 1.07 - 5.86 GPa155 - 850 ksiAverage value: 3.20 GPa Grade Count:23
 2.96475 - 35.0 GPa
@Temperature 80.0 - 175 °C		430.007 - 5080 ksi
@Temperature 176 - 347 °F		Average value: 13.7 GPa Grade Count:2
Shear Strength 6.76 - 137 MPa980 - 19900 psiAverage value: 78.6 MPa Grade Count:51
 11.0 - 164.095 MPa
@Temperature -55.0 - 177 °C		1600 - 23800.0 psi
@Temperature -67.0 - 351 °F		Average value: 58.8 MPa Grade Count:26
Adhesive Bond Strength 5.86 - 24.1 MPa850 - 3500 psiAverage value: 12.8 MPa Grade Count:26
Toughness 51.0 - 541 J37.6 - 399 ft-lbAverage value: 220 J Grade Count:8
 
Electrical PropertiesMetricEnglishComments
Electrical Resistivity 0.00100 - 8.10e+15 ohm-cm0.00100 - 8.10e+15 ohm-cmAverage value: 2.13e+15 ohm-cm Grade Count:31
 1.80e+15 - 1.50e+16 ohm-cm
@Temperature 75.0 - 300 °C		1.80e+15 - 1.50e+16 ohm-cm
@Temperature 167 - 572 °F		Average value: 8.40e+15 ohm-cm Grade Count:1
Dielectric Constant 2.96 - 5.402.96 - 5.40Average value: 4.45 Grade Count:30
 2.95 - 2.95
@Temperature 149 - 149 °C		2.95 - 2.95
@Temperature 300 - 300 °F		Average value: 2.95 Grade Count:1
 2.95 - 2.95
@Frequency 60.0 - 60.0 Hz		2.95 - 2.95
@Frequency 60.0 - 60.0 Hz		Average value: 2.95 Grade Count:1
Dielectric Strength 14.4 - 17.3 kV/mm365 - 440 kV/inAverage value: 16.0 kV/mm Grade Count:28
Dissipation Factor  0.00300 - 0.00300
@Temperature 149 - 149 °C		0.00300 - 0.00300
@Temperature 300 - 300 °F		Average value: 0.00300 Grade Count:1
 0.00300 - 0.00300
@Frequency 60.0 - 60.0 Hz		0.00300 - 0.00300
@Frequency 60.0 - 60.0 Hz		Average value: 0.00300 Grade Count:1
 
Thermal PropertiesMetricEnglishComments
CTE, linear 16.0 - 85.5 µm/m-°C8.89 - 47.5 µin/in-°FAverage value: 50.8 µm/m-°C Grade Count:37
 98.0 - 180 µm/m-°C
@Temperature >=27.0 °C		54.4 - 100 µin/in-°F
@Temperature >=80.6 °F		Average value: 131 µm/m-°C Grade Count:9
Thermal Conductivity 0.140 - 1.28 W/m-K0.972 - 8.88 BTU-in/hr-ft²-°FAverage value: 0.541 W/m-K Grade Count:25
Melting Point -80.0 - 130 °C-112 - 266 °FAverage value: 40.0 °C Grade Count:4
Maximum Service Temperature, Air 25.0 - 260 °C77.0 - 500 °FAverage value: 136 °C Grade Count:61
Softening Point 12.0 - 150 °C53.6 - 302 °FAverage value: 74.4 °C Grade Count:33
Minimum Service Temperature, Air -73.3 - -20.0 °C-100 - -4.00 °FAverage value: -44.0 °C Grade Count:32
Glass Transition Temp, Tg 5.00 - 285 °C41.0 - 545 °FAverage value: 122 °C Grade Count:78
Flash Point 28.0 - 231 °C82.4 - 448 °FAverage value: 122 °C Grade Count:19
Shrinkage 0.250 - 1.60 %0.250 - 1.60 %Average value: 1.17 % Grade Count:6
 
Optical PropertiesMetricEnglishComments
Refractive Index 1.46 - 1.541.46 - 1.54Average value: 1.50 Grade Count:16
Transmission, Visible 90.0 %90.0 %Average value: 90.0 % Grade Count:5
Gardner Color Number 0.200 - 6.000.200 - 6.00Average value: 0.885 Grade Count:33
 
Processing PropertiesMetricEnglishComments
Processing Temperature 25.0 - 170 °C77.0 - 338 °FAverage value: 109 °C Grade Count:13
Moisture Content 0.100 - 0.200 %0.100 - 0.200 %Average value: 0.171 % Grade Count:7
Cure Time 480 - 4320 min8.00 - 72.0 hourAverage value: 2080 min Grade Count:12
 10.02 - 720 min
@Temperature 45.0 - 180 °C		0.1670 - 12.0 hour
@Temperature 113 - 356 °F		Average value: 121 min Grade Count:20
Pot Life 8.00 - 720 min8.00 - 720 minAverage value: 92.7 min Grade Count:30
Gel Time 1.00 - 120 min
@Temperature 60.0 - 240 °C		1.00 - 120 min
@Temperature 140 - 464 °F		Average value: 30.2 min Grade Count:17
Shelf Life 0.750 - 15.0 Month0.750 - 15.0 MonthAverage value: 7.22 Month Grade Count:8
 3.00 - 18.0 Month
@Temperature -18.0 - 10.0 °C		3.00 - 18.0 Month
@Temperature -0.400 - 50.0 °F		Average value: 11.9 Month Grade Count:53
 
Component Elements PropertiesMetricEnglishComments
H2O 0.100 - 0.200 %0.100 - 0.200 %Average value: 0.167 % Grade Count:3

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-32176.html

免责声明: 本文 Overview of materials for Epoxy Cure Resin 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4