- 密度 [g/cm3]: 1.2
- 吸水率 [%]: 0.29
- 缺口冲击强度: 12.3
- 弯曲模量 [MPa]: 17.2
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.20 - 1.50 g/cc | 0.0434 - 0.0542 lb/in³ | ASTM D792 | ||
| Water Absorption | 0.29 % @Temperature 50.0 °C, Time 173000 sec | 0.29 % @Temperature 122 °F, Time 48.0 hour | ASTM D570 | ||
| Linear Mold Shrinkage | 0.0014 cm/cm | 0.0014 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 76.0 MPa | 11000 psi | ASTM D638 | ||
| Flexural Strength | 213 MPa | 30900 psi | at rupture; ASTM D790 | ||
| Flexural Modulus | 17.2 GPa | 2490 ksi | ASTM D790 | ||
| Compressive Strength | 190 MPa | 27600 psi | ASTM D695 | ||
| Izod Impact, Notched | 12.3 J/cm | 23.0 ft-lb/in | ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 2.8 @Frequency 1.00e+6 Hz | 2.8 @Frequency 1.00e+6 Hz | wet; ASTM D150 | ||
| Dielectric Strength | 9.30 kV/mm @Frequency 60.0 Hz | 236 kV/in @Frequency 60.0 Hz | step-by-step, wet; ASTM D149 | ||
| Dissipation Factor | 0.017 @Frequency 1.00e+6 Hz | 0.017 @Frequency 1.00e+6 Hz | wet; ASTM D150 | ||
| Arc Resistance | 120 sec | 120 sec | ASTM D495 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 280 °C | >= 536 °F | Post Baked; ASTM D648A | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Form | Coarse Flake | ||||
| Molding Method | Compression | ||||
| Transfer | |||||