- 吸水率 [%]: 3.1
- 弯曲强度 [MPa]: 2.14
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Water Absorption | 3.1 % @Time 7200 sec | 3.1 % @Time 2.00 hour | boil; cured 2 hours @ 93°C | ||
| 5.0 % @Time 2.59e+6 sec | 5.0 % @Time 720 hour | immersion; cured 90 days @ 25°C | |||
| 5.0 % @Time 2.59e+6 sec | 5.0 % @Time 720 hour | immersion; cured 30 days @ 25°C | |||
| 5.2 % @Time 2.59e+6 sec | 5.2 % @Time 720 hour | immersion; cured 7 days @ 25°C | |||
| Viscosity | 1120 cP | 1120 cP | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 15 @Temperature 75.0 °C | 15 @Temperature 167 °F | cured 2 hrs. @ 93°C | ||
| 45 @Temperature 75.0 °C | 45 @Temperature 167 °F | cured 7 days @ 25°C | |||
| 55 @Temperature 25.0 °C | 55 @Temperature 77.0 °F | cured 2 hrs. @ 93°C | |||
| 94 @Temperature 25.0 °C | 94 @Temperature 77.0 °F | cured 7 days @ 25°C | |||
| Hardness, Shore D | 76 @Temperature 0.000 °C | 76 @Temperature 32.0 °F | cured 7 days @ 25°C | ||
| 85 @Temperature 0.000 °C | 85 @Temperature 32.0 °F | cured 2 hrs. @ 93°C | |||
| 86 @Temperature -60.0 °C | 86 @Temperature -76.0 °F | cured 2 hrs. @ 93°C | |||
| 89 @Temperature -60.0 °C | 89 @Temperature -76.0 °F | cured 7 days @ 25°C | |||
| Tensile Strength, Ultimate | 2.14 MPa | 310 psi | cured 30 days @ 25°C | ||
| 2.28 MPa | 330 psi | cured 7 days @ 25°C | |||
| 2.72 MPa | 395 psi | cured 90 days @ 25°C | |||
| 3.21 MPa | 465 psi | cured 2 hours @ 93°C | |||
| Elongation at Break | 165 % | 165 % | cured 2 hours @ 93°C | ||
| 170 % | 170 % | cured 30 days @ 25°C | |||
| 170 % | 170 % | cured 7 days @ 25°C | |||
| Shear Strength | 6.62 MPa @Temperature 0.000 °C | 960 psi @Temperature 32.0 °F | Tensile, Al/Al lap joint; cured 7 days @ 25°C | ||
| 6.69 MPa @Temperature 25.0 °C | 970 psi @Temperature 77.0 °F | Tensile, Al/Al lap joint; cured 30 days @ 25°C | |||
| 8.96 MPa @Temperature 25.0 °C | 1300 psi @Temperature 77.0 °F | Tensile, Al/Al lap joint; cured 90 days @ 25°C | |||
| 8.998 MPa @Temperature 25.0 °C | 1305 psi @Temperature 77.0 °F | Tensile, Al/Al lap joint; cured 2 hours @ 93°C | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 2.70e+10 ohm-cm @Temperature 25.0 °C | 2.70e+10 ohm-cm @Temperature 77.0 °F | cured 30 days @ 25°C | ||
| 4.20e+10 ohm-cm @Temperature 25.0 °C | 4.20e+10 ohm-cm @Temperature 77.0 °F | cured 90 days @ 25°C | |||
| 6.90e+10 ohm-cm @Temperature 25.0 °C | 6.90e+10 ohm-cm @Temperature 77.0 °F | cured 2 hours @ 93°C | |||
| 9.20e+10 ohm-cm @Temperature 25.0 °C | 9.20e+10 ohm-cm @Temperature 77.0 °F | cured 7 days @ 25°C | |||
| Processing Properties | Metric | English | Comments | ||
| Pot Life | 30 min @Temperature 25.0 °C | 30 min @Temperature 77.0 °F | 200 g | ||
| Descriptive Properties | |||||
| Parts by Weight (pbw) | 100 | AboCast 8110-4 | |||
| 11.5 | AboCure 8110-3 | ||||