- 吸水率 [%]: 2.4
- 弯曲强度 [MPa]: 41.7
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Water Absorption | 2.4 % @Time 2.59e+6 sec | 2.4 % @Time 720 hour | immersion; cured 3 hours @ 100°C | ||
| Viscosity | 2650 cP | 2650 cP | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 80 @Temperature 25.0 °C | 80 @Temperature 77.0 °F | cured 2 hrs. @ 93°C | ||
| 86 @Temperature 0.000 °C | 86 @Temperature 32.0 °F | cured 2 hrs. @ 93°C | |||
| 90 @Temperature -60.0 °C | 90 @Temperature -76.0 °F | cured 2 hrs. @ 93°C | |||
| Tensile Strength, Ultimate | 41.7 MPa | 6050 psi | cured 2 hours @ 93°C | ||
| 61.4 MPa | 8900 psi | cured 8 hours @ 93°C | |||
| Elongation at Break | 14 % | 14 % | cured 8 hours @ 93°C | ||
| 21 % | 21 % | cured 2 hours @ 93°C | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 2.50e+13 ohm-cm @Temperature 100 °C | 2.50e+13 ohm-cm @Temperature 212 °F | cured 2 hours @ 93°C | ||
| 4.80e+15 ohm-cm @Temperature 25.0 °C | 4.80e+15 ohm-cm @Temperature 77.0 °F | cured 2 hours @ 93°C | |||
| Processing Properties | Metric | English | Comments | ||
| Pot Life | 180 min @Temperature 25.0 °C | 180 min @Temperature 77.0 °F | 200 g | ||
| Descriptive Properties | |||||
| Parts by Weight (pbw) | 100 | AboCast 8110-9 | |||
| 43 | AboCure 50-1 | ||||