- 吸水率 [%]: 4.5
- 弯曲强度 [MPa]: 7.93
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Water Absorption | 4.5 % @Time 2.59e+6 sec | 4.5 % @Time 720 hour | immersion; cured 30 days @ 25°C | ||
| 4.6 % @Time 2.59e+6 sec | 4.6 % @Time 720 hour | immersion; cured 7 days @ 25°C | |||
| 4.6 % @Time 7200 sec | 4.6 % @Time 2.00 hour | boil; cured 2 hours @ 93°C | |||
| 4.7 % @Time 2.59e+6 sec | 4.7 % @Time 720 hour | immersion; cured 90 days @ 25°C | |||
| Viscosity | 1050 cP | 1050 cP | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 15 @Temperature 75.0 °C | 15 @Temperature 167 °F | cured 7 days @ 25°C | ||
| 75 @Temperature 25.0 °C | 75 @Temperature 77.0 °F | cured 7 days @ 25°C | |||
| 75 @Temperature 25.0 °C | 75 @Temperature 77.0 °F | cured 2 hrs. @ 93°C | |||
| 85 @Temperature 0.000 °C | 85 @Temperature 32.0 °F | cured 7 days @ 25°C | |||
| 85 @Temperature -60.0 °C | 85 @Temperature -76.0 °F | cured 7 days @ 25°C | |||
| 90 @Temperature 0.000 °C | 90 @Temperature 32.0 °F | cured 2 hrs. @ 93°C | |||
| 90 @Temperature -60.0 °C | 90 @Temperature -76.0 °F | cured 2 hrs. @ 93°C | |||
| Tensile Strength, Ultimate | 7.93 MPa | 1150 psi | cured 30 days @ 25°C | ||
| 8.00 MPa | 1160 psi | cured 7 days @ 25°C | |||
| 13.2 MPa | 1910 psi | cured 90 days @ 25°C | |||
| 15.2 MPa | 2200 psi | cured 2 hours @ 93°C | |||
| Elongation at Break | 125 % | 125 % | cured 30 days @ 25°C | ||
| 130 % | 130 % | cured 2 hours @ 93°C | |||
| 160 % | 160 % | cured 7 days @ 25°C | |||
| Shear Strength | 8.96 MPa @Temperature 0.000 °C | 1300 psi @Temperature 32.0 °F | Tensile, Al/Al lap joint; cured 7 days @ 25°C | ||
| 12.3 MPa @Temperature 25.0 °C | 1780 psi @Temperature 77.0 °F | Tensile, Al/Al lap joint; cured 90 days @ 25°C | |||
| 13.82 MPa @Temperature 25.0 °C | 2005 psi @Temperature 77.0 °F | Tensile, Al/Al lap joint; cured 30 days @ 25°C | |||
| 15.55 MPa @Temperature 25.0 °C | 2255 psi @Temperature 77.0 °F | Tensile, Al/Al lap joint; cured 2 hours @ 93°C | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 3.50e+11 ohm-cm @Temperature 25.0 °C | 3.50e+11 ohm-cm @Temperature 77.0 °F | cured 30 days @ 25°C | ||
| 5.30e+11 ohm-cm @Temperature 25.0 °C | 5.30e+11 ohm-cm @Temperature 77.0 °F | cured 90 days @ 25°C | |||
| 7.50e+11 ohm-cm @Temperature 25.0 °C | 7.50e+11 ohm-cm @Temperature 77.0 °F | cured 2 hours @ 93°C | |||
| 1.10e+12 ohm-cm @Temperature 25.0 °C | 1.10e+12 ohm-cm @Temperature 77.0 °F | cured 7 days @ 25°C | |||
| Processing Properties | Metric | English | Comments | ||
| Pot Life | 20 min @Temperature 25.0 °C | 20 min @Temperature 77.0 °F | 200 g | ||
| Descriptive Properties | |||||
| Parts by Weight (pbw) | 100 | AboCast 8110-2 | |||
| 13 | AboCure 8110-3 | ||||