- 吸水率 [%]: 0.7
- 弯曲强度 [MPa]: 83.08
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Water Absorption | 0.70 % @Time 7200 sec | 0.70 % @Time 2.00 hour | boil; cured 2 hours @ 93°C | ||
| Viscosity | 550 cP | 550 cP | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 83 @Temperature 75.0 °C | 83 @Temperature 167 °F | cured 2 hrs. @ 93°C | ||
| 89 @Temperature 0.000 °C | 89 @Temperature 32.0 °F | cured 2 hrs. @ 93°C | |||
| 89 @Temperature 25.0 °C | 89 @Temperature 77.0 °F | cured 2 hrs. @ 93°C | |||
| 90 @Temperature -60.0 °C | 90 @Temperature -76.0 °F | cured 2 hrs. @ 93°C | |||
| Tensile Strength, Ultimate | 83.08 MPa | 12050 psi | cured 2 hours @ 93°C | ||
| 86.60 MPa | 12560 psi | cured 8 hours @ 93°C | |||
| Elongation at Break | 6.6 % | 6.6 % | cured 8 hours @ 93°C | ||
| 7.1 % | 7.1 % | cured 2 hours @ 93°C | |||
| Shear Strength | 21.2 MPa @Temperature 0.000 °C | 3080 psi @Temperature 32.0 °F | Tensile, Al/Al lap joint; cured 2 hours @ 93°C | ||
| 25.4 MPa @Temperature 25.0 °C | 3690 psi @Temperature 77.0 °F | Tensile, Al/Al lap joint; cured 2 hours @ 93°C | |||
| 34.3 MPa @Temperature 75.0 °C | 4970 psi @Temperature 167 °F | Tensile, Al/Al lap joint; cured 2 hours @ 93°C | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 9.80e+9 ohm-cm @Temperature 150 °C | 9.80e+9 ohm-cm @Temperature 302 °F | cured 2 hours @ 93°C | ||
| 7.60e+10 ohm-cm @Temperature 112 °C | 7.60e+10 ohm-cm @Temperature 234 °F | cured 2 hours @ 93°C | |||
| 1.60e+12 ohm-cm @Temperature 100 °C | 1.60e+12 ohm-cm @Temperature 212 °F | cured 2 hours @ 93°C | |||
| 4.40e+16 ohm-cm @Temperature 25.0 °C | 4.40e+16 ohm-cm @Temperature 77.0 °F | cured 2 hours @ 93°C | |||
| Processing Properties | Metric | English | Comments | ||
| Pot Life | 16 min @Temperature 25.0 °C | 16 min @Temperature 77.0 °F | 200 g | ||
| Descriptive Properties | |||||
| Parts by Weight (pbw) | 100 | AboCast 50-3 | |||
| 13 | AboCure 8110-1 | ||||