- 密度 [g/cm3]: 1.08
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | |||
| Volatiles | 0.00 % | 0.00 % | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 80 | 80 | |||
| Tensile Strength at Break | 15.9 MPa | 2300 psi | |||
| Elongation at Break | 2.8 % | 2.8 % | |||
| Modulus of Elasticity | 0.565 GPa | 82.0 ksi | |||
| Flexural Strength | 27.6 MPa | 4000 psi | |||
| Compressive Strength | 50.3 MPa | 7300 psi | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 60.0 - 120 min @Temperature 93.0 - 105 °C | 1.00 - 2.00 hour @Temperature 199 - 221 °F | |||
| 10080 min @Temperature 20.0 °C | 168.0 hour @Temperature 68.0 °F | (7 Days) | |||
| Pot Life | 50 min @Temperature 25.0 °C | 50 min @Temperature 77.0 °F | 100 g | ||
| Descriptive Properties | |||||
| Color | Gray | ||||
| Hardening Time (min) | 120-240 | at room temperature | |||
| Induction Period (min) | >= 5 | ||||