- 吸水率 [%]: 0.4
- 弯曲强度 [MPa]: 68.3
- 弯曲模量 [MPa]: 2.28
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Water Absorption | 0.40 % @Time 28800 sec | 0.40 % @Time 8.00 hour | boil | ||
| Viscosity | 2000 cP | 2000 cP | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 85 | 85 | |||
| Tensile Strength, Ultimate | 68.3 MPa | 9910 psi | |||
| Flexural Strength | 105 MPa | 15200 psi | |||
| Flexural Modulus | 2.28 GPa | 330 ksi | |||
| Compressive Strength | 116 MPa | 16800 psi | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 105 - 118 °C | 221 - 244 °F | Deflection Temp at unknown load | ||
| Optical Properties | Metric | English | Comments | ||
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 - 240 min @Temperature 100 °C | 2.00 - 4.00 hour @Temperature 212 °F | 2nd step | ||
| 120 - 240 min @Temperature 125 °C | 2.00 - 4.00 hour @Temperature 257 °F | optional 3rd step | |||
| 960 - 1200 min @Temperature 70.0 °C | 16.0 - 20.0 hour @Temperature 158 °F | 1st step | |||
| Pot Life | 4320 min | 4320 min | (3 days) | ||
| Descriptive Properties | |||||
| Acetone Absorption (%) | 1.2 | 3 hr. boil | |||
| Color | Clear | ||||
| Parts by Weight (pbw) | 100 | AboCast | |||
| 73 | AboCure | ||||
| Ultimate Elongation (%) | 5.6 | ||||