- 缺口冲击强度: 0.363
- 断裂伸长率 [%]: 131
- 弯曲强度 [MPa]: 79.22
- 弯曲模量 [MPa]: 3.45
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity Measurement | 60 @Temperature 70.0 °C | 60 @Temperature 158 °F | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 96 | 96 | |||
| Tensile Strength, Ultimate | 79.22 MPa | 11490 psi | |||
| Elongation at Break | 18.2 % | 18.2 % | |||
| Flexural Yield Strength | 131 MPa | 19000 psi | |||
| Flexural Modulus | 3.45 GPa | 500 ksi | |||
| Compressive Yield Strength | 9.928 MPa | 1440 psi | |||
| Compressive Modulus | 1.86 GPa | 270 ksi | |||
| Izod Impact, Notched | 0.363 J/cm | 0.680 ft-lb/in | |||
| Electrical Properties | Metric | English | Comments | ||
| Electrical Resistivity | >= 1.22e+16 ohm-cm | >= 1.22e+16 ohm-cm | |||
| Surface Resistance | >= 7.85e+15 ohm | >= 7.85e+15 ohm | |||
| Dielectric Constant | 3.41 @Frequency 1e+6 Hz | 3.41 @Frequency 1e+6 Hz | |||
| 3.75 @Frequency 1000 Hz | 3.75 @Frequency 1000 Hz | ||||
| 3.78 @Frequency 60 Hz | 3.78 @Frequency 60 Hz | ||||
| Dissipation Factor | 0.0052 @Frequency 60 Hz | 0.0052 @Frequency 60 Hz | |||
| 0.0092 @Frequency 1000 Hz | 0.0092 @Frequency 1000 Hz | ||||
| 0.031 @Frequency 1e+6 Hz | 0.031 @Frequency 1e+6 Hz | ||||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 102 °C | 216 °F | Deflection temperature; load unknown. | ||
| Processing Properties | Metric | English | Comments | ||
| Pot Life | 29 min | 29 min | 500 g at 70°C | ||
| Descriptive Properties | |||||
| Exotherm | 242°C | Peak | |||