| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.58 g/cc | 1.58 g/cc | |||
| Viscosity | 16000 cP | 16000 cP | mixed viscosity | ||
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 89 | 89 | |||
| Flexural Strength | 97.2 MPa | 14100 psi | ASTM D790 | ||
| Shear Strength | 7.826 MPa | 1135 psi | ASTM D1002-94 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 3.00e+15 ohm-cm | 3.00e+15 ohm-cm | |||
| Dielectric Constant | 4.8 @Frequency 1000 Hz | 4.8 @Frequency 1000 Hz | |||
| Dielectric Strength | 18.1 kV/mm | 460 kV/in | |||
| Dissipation Factor | 0.014 | 0.014 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 70.2 µm/m-°C | 39.0 µin/in-°F | |||
| Thermal Conductivity | 0.634 W/m-K | 4.40 BTU-in/hr-ft²-°F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | -55.0 - 120 °C | -67.0 - 248 °F | |||
| Cure Time | 1440 - 2880 min | 24.0 - 48.0 hour | alternate cure, Room Temperature | ||
| 120 min @Temperature 93.3 °C | 2.00 hour @Temperature 200 °F | recommended cure | |||
| 240 min @Temperature 20.0 °C | 4.00 hour @Temperature 68.0 °F | recommended cure | |||
| Pot Life | 120 min | 120 min | 100 gm mass @ 25 °C | ||
| Descriptive Properties | |||||
| Chemical Resistance | Excellent | ||||
| Color | Black | ||||