| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | |||
| Viscosity | 5000 cP | 5000 cP | Mixed Viscosity | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 85 | 85 | |||
| Flexural Strength | 93.1 MPa | 13500 psi | ASTM D790 | ||
| Shear Strength | 31.4 MPa | 4560 psi | ASTM D1002-94 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | |||
| Dielectric Constant | 3.5 @Frequency 1000 Hz | 3.5 @Frequency 1000 Hz | |||
| Dielectric Strength | 15.0 kV/mm | 380 kV/in | |||
| Dissipation Factor | 0.0080 | 0.0080 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 66.6 µm/m-°C @Temperature 20.0 °C | 37.0 µin/in-°F @Temperature 68.0 °F | |||
| Maximum Service Temperature, Air | 177 °C | 350 °F | |||
| Minimum Service Temperature, Air | -55.0 °C | -67.0 °F | |||
| Shrinkage | 0.30 % | 0.30 % | Cure Shrinkage | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min | 2.00 hour | at 150°F (Recommended Cure) | ||
| 2880 min | 48.0 hour | Room Temperature (Alternate Cure) | |||
| Pot Life | 45 min | 45 min | 100 gm mass @ 25°C | ||
| Descriptive Properties | |||||
| Chemical Resistance | Very Good | ||||
| Mix Ratio by Weight | 100:10 | resin:hardener | |||