- 弯曲强度 [MPa]: 33.8
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.81 g/cc | 1.81 g/cc | |||
| Brookfield Viscosity | 7000 cP @Temperature 23.9 °C | 7000 cP @Temperature 75.0 °F | Mixed | ||
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D2566-69 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 86 @Temperature 23.9 °C | 86 @Temperature 75.0 °F | |||
| Tensile Strength, Ultimate | 33.8 MPa | 4900 psi | |||
| Flexural Strength | 55.8 MPa | 8100 psi | |||
| Compressive Strength | 94.5 MPa | 13700 psi | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 66.6 µm/m-°C | 37.0 µin/in-°F | |||
| Heat Distortion Temperature | 54.4 °C | 130 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 1440 - 1800 min @Temperature 24.0 °C | 24.0 - 30.0 hour @Temperature 75.2 °F | |||
| Pot Life | 70 - 80 min @Temperature 24.0 °C | 70 - 80 min @Temperature 75.2 °F | 2 lb. mass | ||
| Descriptive Properties | |||||
| Machinability | Excellent | ||||
| Mix Ratio | 9:1 by weight, 4.6:1 by volume, resin/harder | ||||