- 弯曲强度 [MPa]: 77.2
- 弯曲模量 [MPa]: 3.31
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | |||
| Brookfield Viscosity | 3500 cP @Temperature 23.9 °C | 3500 cP @Temperature 75.0 °F | Mixed | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 86 | 86 | |||
| Tensile Strength, Ultimate | 77.2 MPa | 11200 psi | |||
| Flexural Strength | 131 MPa | 19000 psi | |||
| Flexural Modulus | 3.31 GPa | 480 ksi | |||
| Compressive Strength | 116 MPa | 16800 psi | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 77.8 °C | 172 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 360 - 480 min @Temperature 24.0 °C | 6.00 - 8.00 hour @Temperature 75.2 °F | |||
| Pot Life | 14 - 15 min @Temperature 24.0 °C | 14 - 15 min @Temperature 75.2 °F | 1/2 lb mass | ||
| Descriptive Properties | |||||
| Mix Ratio | 100:20 by weight, 100:22 by volume, resin/harder | ||||