- 弯曲强度 [MPa]: 49.6
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.76 g/cc | 1.76 g/cc | |||
| Brookfield Viscosity | 25000 cP @Temperature 23.9 °C | 25000 cP @Temperature 75.0 °F | Mixed | ||
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D2566-69 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 89 @Temperature 23.9 °C | 89 @Temperature 75.0 °F | |||
| Tensile Strength, Ultimate | 49.6 MPa | 7200 psi | |||
| Flexural Strength | 61.4 MPa | 8900 psi | |||
| Compressive Strength | 113 MPa | 16400 psi | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 720 - 960 min @Temperature 24.0 °C | 12.0 - 16.0 hour @Temperature 75.2 °F | |||
| Pot Life | 30 - 35 min @Temperature 24.0 °C | 30 - 35 min @Temperature 75.2 °F | 4 oz. mass | ||
| Descriptive Properties | |||||
| Machinability | Poor | ||||
| Mix Ratio | 100:9 by weight, 100:15 by volume, resin/harder | ||||