| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Storage Temperature | 25.0 °C | 77.0 °F | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 55.2 MPa | 8010 psi | |||
| Elongation at Break | 3.4 % | 3.4 % | |||
| Tensile Modulus | 2.75 GPa | 399 ksi | |||
| Compressive Strength | 482.8 MPa | 70020 psi | Longitudinal compressive strength as a wet lay-up resin with T-300-W133 fiber. | ||
| Compressive Modulus | 55.15 GPa | 7999 ksi | Longitudinal compressive strength as a wet lay-up resin with T-300-W133 fiber. | ||
| Adhesive Bond Strength | 22.1 MPa @Temperature 93.0 °C | 3210 psi @Temperature 199 °F | Tensile Lap Shear | ||
| 22.8 MPa @Temperature -55.0 °C | 3310 psi @Temperature -67.0 °F | Tensile Lap Shear | |||
| 24.1 MPa @Temperature 25.0 °C | 3500 psi @Temperature 77.0 °F | Tensile Lap Shear | |||
| Peel Strength | 4.40 kN/m | 25.1 pli | Bell Peel | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 177 °C | 351 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 60.0 min @Temperature 66.0 °C | 1.00 hour @Temperature 151 °F | |||
| 7200 - 10100 min @Temperature 25.0 °C | 120 - 168 hour @Temperature 77.0 °F | ||||
| Pot Life | 75 min | 75 min | |||
| Descriptive Properties | |||||
| Consistency | Low Viscosity | ||||
| Form | 2 parts | ||||
| Mix Ratio, Part A:Part B | 100:30 | ||||
| Peel Strength | Moderate | ||||