| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Storage Temperature | 25.0 °C | 77.0 °F | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 36.6 MPa | 5310 psi | |||
| Elongation at Break | 7.7 % | 7.7 % | |||
| Tensile Modulus | 2.20 GPa | 319 ksi | |||
| Adhesive Bond Strength | 6.90 MPa @Temperature 93.0 °C | 1000 psi @Temperature 199 °F | Tensile Lap Shear | ||
| 27.6 MPa @Temperature -55.0 °C | 4000 psi @Temperature -67.0 °F | Tensile Lap Shear | |||
| 31.0 MPa @Temperature 25.0 °C | 4500 psi @Temperature 77.0 °F | Tensile Lap Shear | |||
| Peel Strength | 13.4 kN/m | 76.5 pli | Bell Peel | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 93.0 °C | 199 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 60.0 min @Temperature 82.0 °C | 1.00 hour @Temperature 180 °F | |||
| 7200 - 10100 min @Temperature 25.0 °C | 120 - 168 hour @Temperature 77.0 °F | ||||
| Pot Life | 40 min | 40 min | |||
| Descriptive Properties | |||||
| Consistency | Thixotropic | ||||
| Form | 2 parts | ||||
| Mix Ratio, Part A:Part B | 100:44 | ||||
| Peel Strength | High | ||||