- 密度 [g/cm3]: 0.8
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.800 g/cc | 0.0289 lb/in³ | |
| Density | 0.800 g/cc | 0.0289 lb/in³ | |
| Thickness | 76.2 microns | 3.00 mil | Nominal |
| 78.7 microns | 3.10 mil | Typical; ASTM D374 | |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 11 % | 11 % | ASTM D828 |
| Film Elongation at Break, TD | 8.0 % | 8.0 % | ASTM D828 |
| Tear Strength, Total | 8.00 N | 1.80 lb (f) | Initial in TD; ASTM D1004 |
| 16.0 N | 3.60 lb (f) | Initial in MD; ASTM D1004 | |
| Elmendorf Tear Strength, MD | 1.54 g/micron | 39.0 g/mil | Calculated from mfr's report of 1.2 N per TAPPI-414 and the typical thickness |
| Elmendorf Tear Strength, TD | 2.99 g/micron | 76.0 g/mil | Calculated from mfr's report of 2.3 N per TAPPI-414 and the typical thickness |
| Film Tensile Strength at Break, MD | 82.6 MPa | 12000 psi | Calculated from mfr's report of 65 N/cm per ASTM D828 and the typical thickness |
| Film Tensile Strength at Break, TD | 40.6 MPa | 5890 psi | Calculated from mfr's report of 32 N/cm per ASTM D828 and the typical thickness |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.00e+16 ohm-cm | 2.00e+16 ohm-cm | 50% RH; tested on 10 mil thickness sample; ASTM D257 |
| Surface Resistivity per Square | 2.00e+16 ohm | 2.00e+16 ohm | tested on 10 mil thickness sample; ASTM D257 |
| Dielectric Constant | 1.6 @Frequency 60 Hz | 1.6 @Frequency 60 Hz | ASTM D150 |
| Dielectric Strength | 22.0 kV/mm | 559 kV/in | AC Rapid Rise; ASTM D149 |
| 39.0 kV/mm | 991 kV/in | Full-wave Impulse; ASTM D3426 | |
| Dissipation Factor | 0.0050 @Frequency 60 Hz | 0.0050 @Frequency 60 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| Thermal Conductivity | 0.114 W/m-K @Temperature 150 °C | 0.791 BTU-in/hr-ft²-°F @Temperature 302 °F | |
| Maximum Service Temperature, Air | 220 °C | 428 °F | 220°C insulation by UL, the US Navy, and other tests |
| Oxygen Index | 27 - 32 % | 27 - 32 % | Range at RT for Type 410; depends on thickness and density |
| Shrinkage, MD | 1.1 % | 1.1 % | at 300°C |
| Shrinkage, TD | 0.00 % | 0.00 % | at 300°C |