- 密度 [g/cm3]: 0.176
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.176 g/cc | 0.00637 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Compressive Yield Strength | >= 15.2 MPa | >= 2200 psi | Bare, min |
| >= 15.9 MPa | >= 2300 psi | Stabilized, min | |
| 17.9 MPa | 2600 psi | Bare, typ | |
| 18.6 MPa | 2700 psi | Stabilized, typ | |
| Shear Modulus | 0.110 GPa | 16.0 ksi | Plate Shear, W Direction, typ, preliminary value obtained from limited testing |
| 0.193 GPa | 28.0 ksi | Plate Shear, L Direction, typ, preliminary value obtained from limited testing | |
| Shear Strength | >= 2.48 MPa | >= 360 psi | Plate Shear, W Direction, min, preliminary value obtained from limited testing |
| 3.10 MPa | 450 psi | Plate Shear, W Direction, typ, preliminary value obtained from limited testing | |
| >= 3.52 MPa | >= 510 psi | Plate Shear, L Direction, min, preliminary value obtained from limited testing | |
| 4.41 MPa | 640 psi | Plate Shear, L Direction, typ, preliminary value obtained from limited testing | |