- 密度 [g/cm3]: 0.0801
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.0801 g/cc | 0.00289 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Compressive Yield Strength | >= 3.00 MPa | >= 435 psi | Bare, min |
| >= 3.24 MPa | >= 470 psi | Stabilized, min | |
| 3.79 MPa | 550 psi | Bare, typ | |
| 4.14 MPa | 600 psi | Stabilized, typ | |
| Shear Modulus | 0.0345 GPa | 5.00 ksi | Plate Shear, W Direction, typ, preliminary value obtained from limited testing |
| 0.0758 GPa | 11.0 ksi | Plate Shear, L Direction, typ, preliminary value obtained from limited testing | |
| Shear Strength | >= 0.965 MPa | >= 140 psi | Plate Shear, W Direction, min, preliminary value obtained from limited testing |
| 1.24 MPa | 180 psi | Plate Shear, W Direction, typ, preliminary value obtained from limited testing | |
| >= 1.93 MPa | >= 280 psi | Plate Shear, L Direction, min, preliminary value obtained from limited testing | |
| 2.48 MPa | 360 psi | Plate Shear, L Direction, typ, preliminary value obtained from limited testing | |