- 密度 [g/cm3]: 0.144
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.144 g/cc | 0.00521 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Compressive Yield Strength | >= 8.96 MPa | >= 1300 psi | Bare, min |
| >= 9.58 MPa | >= 1390 psi | Stabilized, min | |
| 11.7 MPa | 1700 psi | Bare, typ | |
| 12.93 MPa | 1875 psi | Stabilized, typ | |
| Shear Modulus | 0.0655 GPa | 9.50 ksi | Plate Shear, W Direction, typ, preliminary value obtained from limited testing |
| 0.110 GPa | 16.0 ksi | Plate Shear, L Direction, typ, preliminary value obtained from limited testing | |
| Shear Strength | >= 1.38 MPa | >= 200 psi | Plate Shear, W Direction, min, preliminary value obtained from limited testing |
| 1.97 MPa | 285 psi | Plate Shear, W Direction, typ, preliminary value obtained from limited testing | |
| >= 2.83 MPa | >= 410 psi | Plate Shear, L Direction, min, preliminary value obtained from limited testing | |
| 3.62 MPa | 525 psi | Plate Shear, L Direction, typ, preliminary value obtained from limited testing | |