- 密度 [g/cm3]: 1.2
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 63.5 microns | 2.50 mil | Side 1; Arlon SQA-TMS-003 | ||
| 76.2 microns | 3.00 mil | Interleave | |||
| 140 microns | 5.50 mil | Substrate; Arlon SQA-TMS-003 | |||
| 229 microns | 9.00 mil | Side 2; Arlon SQA-TMS-003 | |||
| 432 microns | 17.0 mil | Overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 73 | 73 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 5.17 MPa | 750 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 252 % | 252 % | Silicone Property; ASTM D412 | ||
| Tear Strength | 12.8 kN/m | 73.0 pli | Die B, Silicone Property; ASTM D624 | ||
| Peel Strength | 0.263 kN/m | 1.50 pli | Bond Strength (S2 to S2); Arlon SQA-TMS-011 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 177 °C | 0.250 hour @Pressure 50.0 psi, Temperature 350 °F | Recommended Cure Cycle | ||
| Shelf Life | 3.00 Month @Temperature 7.22 °C | 3.00 Month @Temperature 45.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Black | ||||
| Black | Substrate | ||||
| Gray | Substrate | ||||
| Total Product Weight (oz/yd2) | 18.3 | Arlon SQA-TMS-025 | |||