- 密度 [g/cm3]: 1.5
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | Fluorosilicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 63.5 microns | 2.50 mil | Interleave | ||
| 127 microns | 5.00 mil | Substrate; Arlon SQA-TMS-003 | |||
| 127 microns | 5.00 mil | Side 2; Arlon SQA-TMS-003 | |||
| 127 microns | 5.00 mil | Side 1; Arlon SQA-TMS-003 | |||
| 381 microns | 15.0 mil | Overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 56 | 56 | Fluorosilicone Property; ASTM D2240 | ||
| Tensile Strength | 7.10 MPa | 1030 psi | Fluorosilicone Property; ASTM D412 | ||
| Elongation at Break | 410 % | 410 % | Fluorosilicone Property; ASTM D412 | ||
| Tear Strength | 19.1 kN/m | 109 pli | Die B, Fluorosilicone Property; ASTM D624 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Shelf Life | 60.0 Month @Temperature 21.1 °C | 60.0 Month @Temperature 70.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Green | ||||
| Fuel Resistance | 17.5 | Fuel A Resistance, Product Property, ASTM D471 | |||
| 23.2 | Fuel C Resistance, Fluorosilicone Property, ASTM D471 | ||||
| 26.6 | Fuel C Resistance, Product Property, ASTM D471 | ||||
| 8.1 | Fuel CM85 Resistance, Fluorosilicone Property, ASTM D471 | ||||
| 8.9 | Fuel CM85 Resistance, Product Property, ASTM D471 | ||||
| 9.6 | Fuel A Resistance, Fluorosilicone Property, ASTM D471 | ||||
| Mullen Burst Strength | 213 | ASTM D751 | |||
| Plasticity | 2.3 mm | Arlon SQA-TMS-005 | |||
| 3.21 mm | Arlon SQA-TMS-005 | ||||
| Uncoated Fabric Break Strength | 109 ppiw | Fill Strength, ASTM D751 | |||
| 155 ppiw | Warp Strength, ASTM D751 | ||||