- 密度 [g/cm3]: 1.2
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 76.2 microns | 3.00 mil | Interleave | ||
| 140 microns | 5.50 mil | Substrate; Arlon SQA-TMS-003 | |||
| 368 microns | 14.5 mil | Side 1; Arlon SQA-TMS-003 | |||
| 508 microns | 20.0 mil | Overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 4.92 MPa | 714 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 225 % | 225 % | Silicone Property; ASTM D412 | ||
| Tear Strength | 12.8 kN/m | 73.0 pli | Die B, Silicone Property; ASTM D624 | ||
| Peel Strength | 0.508 kN/m | 2.90 pli | Bond Strength (S1 to S1); Arlon SQA-TMS-011 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.84 ohm-cm | 1.84 ohm-cm | ASTM D991 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 177 °C | 0.250 hour @Pressure 50.0 psi, Temperature 350 °F | Recommended Cure Cycle | ||
| Shelf Life | 3.00 Month @Temperature 7.22 °C | 3.00 Month @Temperature 45.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Black | ||||
| Black | Substrate | ||||
| Gray | Substrate | ||||
| Total Product Weight (oz/yd2) | 15.6 | Arlon SQA-TMS-025 | |||