- 密度 [g/cm3]: 1.88
- 吸水率 [%]: 0.06
- 弯曲强度 [MPa]: 65.0
- 弯曲模量 [MPa]: 20.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.650 g/cc | 0.0235 lb/in³ | Powder; ISO 60 | ||
| Density | 1.88 g/cc | 0.0679 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.060 % | 0.060 % | ISO 62 | ||
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ISO 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 95 | 95 | ISO 2039/2 | ||
| Tensile Strength, Ultimate | 65.0 MPa | 9430 psi | ISO 527 | ||
| Flexural Strength | 135 MPa | 19600 psi | ISO 178 | ||
| Flexural Modulus | 20.0 GPa | 2900 ksi | ISO 178 | ||
| Compressive Strength | 265 MPa | 38400 psi | ISO 604 | ||
| Charpy Impact, Notched | 0.450 J/cm² | 2.14 ft-lb/in² | ISO 179 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 13.5 kV/mm | 343 kV/in | 3 mm; IEC 243 | ||
| Arc Resistance | 185 sec | 185 sec | ASTM D495 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 17.0 µm/m-°C @Temperature 23.0 °C | 9.44 µin/in-°F @Temperature 73.4 °F | TMA | ||
| CTE, linear, Transverse to Flow | 39.0 µm/m-°C @Temperature 20.0 °C | 21.7 µin/in-°F @Temperature 68.0 °F | TMA | ||
| Thermal Conductivity | 0.740 W/m-K | 5.14 BTU-in/hr-ft²-°F | ASTM F433 | ||
| Maximum Service Temperature, Air | 150 °C | 302 °F | UL Temperature Index; UL 746B | ||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 282 °C | >= 540 °F | Post Baked; ISO 75 A | ||
| Flammability, UL94 | V-0 | V-0 | 3.2mm | ||
| V-0 | V-0 | 1.6 mm | |||
| Descriptive Properties | |||||
| Available Molding Grades | Compression, Transfer, Injection | ||||
| Color | Black | ||||
| Form | Flake | ||||