- 密度 [g/cm3]: 0.0961
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.0961 g/cc | 0.00347 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Compressive Yield Strength | >= 4.48 MPa | >= 650 psi | Bare, min |
| >= 5.52 MPa | >= 800 psi | Stabilized, min | |
| 5.72 MPa | 830 psi | Bare, typ | |
| 6.89 MPa | 1000 psi | Stabilized, typ | |
| Compressive Modulus | 0.689 GPa | 100 ksi | Stabilized, typ |
| Shear Modulus | 0.0814 GPa | 11.8 ksi | Plate Shear, W Direction, typ |
| 0.159 GPa | 23.0 ksi | Plate Shear, L Direction, typ | |
| Shear Strength | >= 1.45 MPa | >= 210 psi | Plate Shear, W Direction, min |
| 1.93 MPa | 280 psi | Plate Shear, W Direction, typ | |
| >= 2.76 MPa | >= 400 psi | Plate Shear, L Direction, min | |
| 3.24 MPa | 470 psi | Plate Shear, L Direction, typ | |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 177 °C | 350 °F | High strength retained |