- 弯曲强度 [MPa]: 20.9
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Mooney Viscosity | 86 @Temperature 121 °C | 86 @Temperature 250 °F | ML-10 (gum) |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 73 | 73 | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| Tensile Strength, Ultimate | 20.9 MPa | 3030 psi | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| Elongation at Break | 174 % | 174 % | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| Modulus of Elasticity | 0.000750 GPa | 0.109 ksi | 10% Modulus, Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| 100% Modulus | 0.00730 GPa | 1.06 ksi | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| Thermal Properties | Metric | English | Comments |
| Glass Transition Temp, Tg | -15.8 °C | 3.56 °F | DSC, modulated, midpoint |