- 密度 [g/cm3]: 1.046
- 弯曲强度 [MPa]: 17.4
- 脆化温度 [℃]: -40.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.046 g/cc | 0.03779 lb/in³ | |
| Mooney Viscosity | 76 @Temperature 100 °C | 76 @Temperature 212 °F | ML 1 + 4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 64 | 64 | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tensile Strength, Ultimate | 17.4 MPa | 2520 psi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Elongation at Break | 383 % | 383 % | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 100% Modulus | 0.00250 GPa | 0.363 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 200% Modulus | 0.00660 GPa | 0.957 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 300% Modulus | 0.0116 GPa | 1.68 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tear Strength | 31.7 kN/m | 181 pli | Die C, Vulcanizate, Press cured, TC95 +3min at 160°C |
| Compression Set | 20 % @Temperature 125 °C | 20 % @Temperature 257 °F | Pellets cured MDR TC95 + 15 min at 160°C, 70 hr at 125°C; Method B |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -40.0 °C | -40.0 °F | Temperature Retraction, TR-10 |