- 脆化温度 [℃]: -60.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.86 g/cc | 1.86 g/cc | |||
| Mooney Viscosity | 95 @Temperature 121 °C | 95 @Temperature 250 °F | ML 1+ 10 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 68 | 68 | Press Cure 10 Minutes @ 177°C | ||
| 70 | 70 | Post Cure 16 Hours @ 230°C | |||
| Tensile Strength at Break | 11.9 MPa | 1730 psi | Press Cure 10 Minutes @ 177°C | ||
| 13.3 MPa | 1930 psi | Post Cure 16 Hours @ 230°C | |||
| Elongation at Break | 175 % | 175 % | Post Cure 16 Hours @ 230°C | ||
| 180 % | 180 % | Press Cure 10 Minutes @ 177°C | |||
| 100% Modulus | 0.00610 GPa | 0.885 ksi | Press Cure 10 Minutes @ 177°C | ||
| 0.00610 GPa | 0.885 ksi | Post Cure 16 Hours @ 230°C | |||
| Compression Set | 15 % @Treatment Temp. 150 °C, Time 252000 sec | 15 % @Treatment Temp. 302 °F, Time 70.0 hour | Method B, -214 O-rings, Aged 70 Hours; ASTM D395 | ||
| 26 % @Treatment Temp. 200 °C, Time 252000 sec | 26 % @Treatment Temp. 392 °F, Time 70.0 hour | Method B, -214 O-rings, Aged 70 Hours; ASTM D395 | |||
| 32 % @Treatment Temp. 200 °C, Time 605000 sec | 32 % @Treatment Temp. 392 °F, Time 168 hour | Method B, -214 O-rings, Aged 168 Hours; ASTM D395 | |||
| Thermal Properties | Metric | English | Comments | ||
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | TR10 | ||
| Brittleness Temperature | -60.0 °C | -76.0 °F | |||
| Glass Transition Temp, Tg | -40.0 °C | -40.0 °F | |||
| Transformation Temperature | -40.0 °C | -40.0 °F | TR10; ASTM D1329 | ||
| Component Elements Properties | Metric | English | Comments | ||
| Fluorine, F | 67.1 % | 67.1 % | |||
| Descriptive Properties | |||||
| Color | White | ||||
| Form | Crumb | ||||
| MH, Maximum Toque | 14.0 Inch-lb | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C | |||
| ML, Minimum Torque | 4.0 Inch-lb | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C | |||
| t2, Time to 2 Inch-lb Rise from Minimum | 0.5 Minutes | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C | |||
| t'50, Time to 50% Cure | 0.7 Minutes | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C | |||
| t'90, Time to 90% Cure | 2.3 Minutes | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C | |||