| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.89 g/cc | 1.89 g/cc | |||
| Mooney Viscosity | 38 @Temperature 121 °C | 38 @Temperature 250 °F | ML 1+10 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 72 | 72 | Press cure 15 minutes@ 180°C | ||
| 75 | 75 | Post cure 2 hours @ 180°C | |||
| Tensile Strength at Break | 18.0 MPa | 2610 psi | Press cure 15 minutes@ 180°C | ||
| 22.0 MPa | 3190 psi | Post cure 2 hours @ 180°C | |||
| Elongation at Break | 210 % | 210 % | Post cure 2 hours @ 180°C | ||
| 220 % | 220 % | Press cure 15 minutes@ 180°C | |||
| 100% Modulus | 0.00450 GPa | 0.653 ksi | Press cure 15 minutes@ 180°C | ||
| 0.00580 GPa | 0.841 ksi | Post cure 2 hours @ 180°C | |||
| Compression Set | 30 % @Treatment Temp. 200 °C, Time 252000 sec | 30 % @Treatment Temp. 392 °F, Time 70.0 hour | Method B; ASTM D395 | ||
| Thermal Properties | Metric | English | Comments | ||
| Transformation Temperature | -6.00 °C | 21.2 °F | TR10; ASTM D1329 | ||
| Component Elements Properties | Metric | English | Comments | ||
| Fluorine, F | 69.5 % | 69.5 % | |||
| Descriptive Properties | |||||
| Color | White | ||||
| MH, Maximum Toque | 22.0 inch-lb | 100 cpm, 0.5° Arc, 12 Minutes @ 177°C | |||
| ML, Minimum Torque | 0.7 inch-lb | 100 cpm, 0.5° Arc, 12 Minutes @ 177°C | |||
| t2, Time to 2 Inch-lb Rise from Minimum | 1 Minute | 100 cpm, 0.5° Arc, 12 Minutes @ 177°C | |||
| t'50, Time to 50% Cure | 2.3 Minutes | 100 cpm, 0.5° Arc, 12 Minutes @ 177°C | |||
| t'90, Time to 90% Cure | 5 Minutes | 100 cpm, 0.5° Arc, 12 Minutes @ 177°C | |||