- 密度 [g/cm3]: 0.8
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.800 g/cc | 0.0289 lb/in³ | M1433B; ASTM D1475-85 | ||
| 0.980 g/cc | 0.0354 lb/in³ | Mixed; ASTM D1475-85 | |||
| 1.04 g/cc | 0.0376 lb/in³ | M1433A; ASTM D1475-85 | |||
| Solids Content | 9.0 % | 9.0 % | M1433B; by weight; ASTM D2369-87 Modified | ||
| 50 % | 50 % | Mixed; by volume; ASTM D2369-87 Modified | |||
| 58 % | 58 % | Mixed; by weight; ASTM D2369-87 Modified | |||
| 65 % | 65 % | M1433A; by volume; ASTM D2369-87 Modified | |||
| 71 % | 71 % | M1433A; by weight; ASTM D2369-87 Modified | |||
| Volatile Organic Compounds (VOC) Content | 300 g/l | 300 g/l | M1433A; ASTM D3960-87 | ||
| 420 g/l | 420 g/l | Mixed; ASTM D3960-87 | |||
| 766 g/l | 766 g/l | M1433B; ASTM D3960-87 | |||
| Brookfield Viscosity | 0.89 cP @Temperature 25.0 °C | 0.89 cP @Temperature 77.0 °F | M1433B; typical of water thin materials; ASTM D2196-86; LVT | ||
| 200 - 600 cP @Temperature 25.0 °C | 200 - 600 cP @Temperature 77.0 °F | Mixed; ASTM D2196-86; LVT, Spindle #3 @ 30rpm | |||
| 700 - 1500 cP @Temperature 25.0 °C | 700 - 1500 cP @Temperature 77.0 °F | M1433A; ASTM D2196-86; LVT, Spindle #4 @ 30rpm | |||
| Thermal Properties | Metric | English | Comments | ||
| Flash Point | 18.9 °C | 66.0 °F | M1433A; Setaflash, Closed Cup; ASTM D3278-82 | ||
| 43.3 °C | 110 °F | M1433B; Setaflash, Closed Cup; ASTM D3278-82 | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 240 - 360 min @Temperature 23.0 °C | 4.00 - 6.00 hour @Temperature 73.4 °F | |||
| Pot Life | 120 min | 120 min | |||
| Shelf Life | 6.00 Month @Temperature 15.6 °C | 6.00 Month @Temperature 60.1 °F | |||
| Descriptive Properties | |||||
| Coating Film Dry Weight (gm/ft²/mil) | 2.69 | ||||
| Mix Ratio | 3.7:1 | by weight | |||
| 3:1 | by volume | ||||