- 密度 [g/cm3]: 0.8
- 弯曲强度 [MPa]: 79.3
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.800 g/cc | 0.0289 lb/in³ | ASTM D3574A |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 50 | 50 | ASTM D2240 |
| Tensile Strength, Ultimate | 79.3 MPa | 11500 psi | ASTM D3574E |
| Elongation at Break | 625 % | 625 % | ASTM 3457E |
| 100% Modulus | 0.00131 GPa | 0.190 ksi | ASTM D3574E |
| 200% Modulus | 0.00210 GPa | 0.305 ksi | ASTM D3574E |
| 300% Modulus | 0.00314 GPa | 0.455 ksi | ASTM D3574E |
| Compressive Yield Strength | 0.480 MPa | 69.6 psi | at 10% deflection; ASTM D3574C |
| 0.720 MPa | 104 psi | at 20% deflection; ASTM D3574C | |
| 1.03 MPa | 149 psi | at 30% deflection; ASTM D3574C | |
| Resilience | 40 | 40 | Bashore Rebound; ASTM 2632D |
| Tear Strength Test | 130 | 130 | lb; Die C; ASTM 3457F |