- 密度 [g/cm3]: 0.48
- 弯曲强度 [MPa]: 11.4
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.480 g/cc | 0.0173 lb/in³ | ASTM D3574A |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 20 | 20 | ASTM D2240 |
| Tensile Strength, Ultimate | 11.4 MPa | 1650 psi | ASTM D3574E |
| Elongation at Break | 350 % | 350 % | ASTM 3457E |
| 100% Modulus | 0.000414 GPa | 0.0600 ksi | ASTM D3574E |
| 200% Modulus | 0.00103 GPa | 0.149 ksi | ASTM D3574E |
| 300% Modulus | 0.00134 GPa | 0.194 ksi | ASTM D3574E |
| Compressive Yield Strength | 0.0700 MPa | 10.2 psi | at 10% deflection; ASTM D3574C |
| 0.121 MPa | 17.5 psi | at 20% deflection; ASTM D3574C | |
| 0.160 MPa | 23.2 psi | at 30% deflection; ASTM D3574C | |
| Resilience | 52 | 52 | Bashore Rebound; ASTM 2632D |
| Tear Strength Test | 43 | 43 | lb; Die C; ASTM 3457F |