- 拉伸强度 [MPa]: 23.64
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 70 | 70 | |
| Tensile Strength, Yield | 23.64 MPa | 3429 psi | |
| Elongation at Yield | 363 % | 363 % | |
| 100% Modulus | 0.00319 GPa | 0.462 ksi | |
| 200% Modulus | 0.01084 GPa | 1.572 ksi | |
| 300% Modulus | 0.01934 GPa | 2.805 ksi | |
| Tear Strength | 55.7 kN/m | 318 pli | Die C |
| Processing Properties | Metric | English | Comments |
| Cure Time | 15.0 min @Temperature 160 °C | 0.250 hour @Temperature 320 °F | |