- 拉伸强度 [MPa]: 29.32
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 78 | 78 | |
| Tensile Strength, Yield | 29.32 MPa | 4252 psi | |
| Elongation at Yield | 521 % | 521 % | |
| 100% Modulus | 0.00476 GPa | 0.690 ksi | |
| 200% Modulus | 0.0110 GPa | 1.60 ksi | |
| 300% Modulus | 0.01747 GPa | 2.534 ksi | |
| Tear Strength | 66.2 kN/m | 378 pli | |
| Taber Abrasion, mg/1000 Cycles | 6.5 @Load 1.00 kg | 6.5 @Load 2.20 lb | H-18 wheel |
| Compression Set | 44.2 % @Temperature 70.0 °C, Time 79200 sec | 44.2 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 15.0 min @Temperature 154 °C | 0.250 hour @Temperature 309 °F | |