- 拉伸强度 [MPa]: 24.12
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 80 | 80 | |
| Tensile Strength, Yield | 24.12 MPa | 3499 psi | |
| Elongation at Yield | 495 % | 495 % | |
| 100% Modulus | 0.00560 GPa | 0.812 ksi | |
| 200% Modulus | 0.01193 GPa | 1.731 ksi | |
| 300% Modulus | 0.01739 GPa | 2.522 ksi | |
| Tear Strength | 63.9 kN/m | 365 pli | Die C |
| Processing Properties | Metric | English | Comments |
| Cure Time | 15.0 min @Temperature 155 °C | 0.250 hour @Temperature 311 °F | |