- 拉伸强度 [MPa]: 29.19
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 65 | 65 | |
| Tensile Strength, Yield | 29.19 MPa | 4234 psi | |
| Elongation at Yield | 397 % | 397 % | |
| 100% Modulus | 0.00279 GPa | 0.405 ksi | |
| 200% Modulus | 0.009604 GPa | 1.393 ksi | |
| 300% Modulus | 0.02099 GPa | 3.045 ksi | |
| Tear Strength | 58.3 kN/m | 333 pli | Die C |
| Processing Properties | Metric | English | Comments |
| Cure Time | 15.0 min @Temperature 160 °C | 0.250 hour @Temperature 320 °F | |