- 拉伸强度 [MPa]: 17.9
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 88 | 88 | |
| Tensile Strength, Yield | 17.9 MPa | 2600 psi | |
| Elongation at Yield | 350 % | 350 % | |
| 100% Modulus | 0.00896 GPa | 1.30 ksi | |
| 200% Modulus | 0.0150 GPa | 2.17 ksi | |
| 300% Modulus | 0.0169 GPa | 2.45 ksi | |
| Tear Strength | 63.0 kN/m | 359 pli | Die C |
| Processing Properties | Metric | English | Comments |
| Cure Time | 15.0 min @Temperature 155 °C | 0.250 hour @Temperature 311 °F | |