- 拉伸强度 [MPa]: 28.76
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 60 | 60 | |
| Tensile Strength, Yield | 28.76 MPa | 4171 psi | |
| Elongation at Yield | 564 % | 564 % | |
| 100% Modulus | 0.00227 GPa | 0.329 ksi | |
| 200% Modulus | 0.00498 GPa | 0.723 ksi | |
| 300% Modulus | 0.008770 GPa | 1.272 ksi | |
| Tear Strength | 59.9 kN/m | 342 pli | |
| Taber Abrasion, mg/1000 Cycles | 7.0 @Load 1.00 kg | 7.0 @Load 2.20 lb | H-18 wheel |
| Compression Set | 51.7 % @Temperature 70.0 °C, Time 79200 sec | 51.7 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 10.0 min @Temperature 154 °C | 0.167 hour @Temperature 309 °F | |