- 拉伸强度 [MPa]: 23.4
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | 68 | 68 | |||
| 69 | 69 | after 7 days at 100ºC | |||
| Tensile Strength, Yield | 23.4 MPa | 3400 psi | after 7 days at 100ºC | ||
| 29.48 MPa | 4275 psi | ||||
| Elongation at Break | 290 % | 290 % | after 7 days at 100ºC | ||
| 460 % | 460 % | ||||
| 300% Modulus | 0.0152 GPa | 2.20 ksi | |||
| Abrasion | 380 | 380 | NBS Index | ||
| Compression Set | 21 % @Temperature 70.0 °C, Time 79200 sec | 21 % @Temperature 158 °F, Time 22.0 hour | Method B | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 60.0 min @Temperature 142 °C | 1.00 hour @Temperature 287 °F | |||
| Descriptive Properties | |||||
| ?T, Platen (ºC) | 58 | ||||
| Heat Build-up, Internal Temp (ºC) | 125 | Goodrich Flexometer | |||