- 拉伸强度 [MPa]: 40.0
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | 66 | 66 | |||
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | |||
| Elongation at Yield | 570 % | 570 % | |||
| 100% Modulus | 0.00241 GPa | 0.350 ksi | |||
| 300% Modulus | 0.0138 GPa | 2.00 ksi | |||
| Tear Strength | 48.2 kN/m | 275 pli | Graves | ||
| Abrasion | 350 | 350 | NBS Index | ||
| Compression Set | 35 % @Temperature 70.0 °C, Time 79200 sec | 35 % @Temperature 158 °F, Time 22.0 hour | Method B | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 30.0 min @Temperature 142 °C | 0.500 hour @Temperature 287 °F | |||
| Descriptive Properties | |||||
| 500% Modulus (ksi) | 4.5 | ||||
| Mooney Scorch | >= 32 | at 250ºF; 23 minutes to a 10 point rise | |||