- 拉伸强度 [MPa]: 10.3
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 84 | 84 | heat aged one week at 300ºF |
| 86 | 86 | ||
| 89 | 89 | heat aged 70 hours at 300ºF | |
| Tensile Strength, Yield | 10.3 MPa | 1500 psi | heat aged one week at 300ºF |
| 14.5 MPa | 2100 psi | heat aged 70 hours at 300ºF | |
| 24.9 MPa | 3610 psi | ||
| Elongation at Yield | 220 % | 220 % | heat aged 70 hours at 300ºF |
| 230 % | 230 % | heat aged one week at 300ºF | |
| 280 % | 280 % | ||
| 100% Modulus | 0.00483 GPa | 0.700 ksi | heat aged one week at 300ºF |
| 0.00655 GPa | 0.950 ksi | heat aged 70 hours at 300ºF | |
| 0.00993 GPa | 1.44 ksi | ||
| 200% Modulus | 0.00793 GPa | 1.15 ksi | heat aged one week at 300ºF |
| 0.0131 GPa | 1.90 ksi | heat aged 70 hours at 300ºF | |
| 0.0207 GPa | 3.00 ksi | ||
| Processing Properties | Metric | English | Comments |
| Cure Time | 30.0 min @Temperature 152 °C | 0.500 hour @Temperature 305 °F | |