- 拉伸强度 [MPa]: 27.9
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | >= 64 | >= 64 | |
| Tensile Strength, Yield | 27.90 MPa | 4046 psi | |
| Elongation at Yield | 541 % | 541 % | |
| 100% Modulus | 0.00260 GPa | 0.377 ksi | |
| 200% Modulus | 0.00600 GPa | 0.870 ksi | |
| 300% Modulus | 0.01030 GPa | 1.494 ksi | |
| Tear Strength | 39.3 kN/m | 224 pli | Die C |
| Compression Set | 33.2 % @Temperature 70.0 °C, Time 79200 sec | 33.2 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 9.50 min @Temperature 68.3 °C | 0.158 hour @Temperature 155 °F | |