- 拉伸强度 [MPa]: 30.19
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | >= 65 | >= 65 | |
| Tensile Strength, Yield | 30.19 MPa | 4379 psi | |
| Elongation at Yield | 559 % | 559 % | |
| 100% Modulus | 0.00270 GPa | 0.392 ksi | |
| 200% Modulus | 0.00580 GPa | 0.841 ksi | |
| 300% Modulus | 0.01030 GPa | 1.494 ksi | |
| Tear Strength | 35.0 kN/m | 200 pli | Die C |
| Compression Set | 32.2 % @Temperature 70.0 °C, Time 79200 sec | 32.2 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 10.0 min @Temperature 155 °C | 0.167 hour @Temperature 311 °F | |