- 拉伸强度 [MPa]: 30.23
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | >= 66 | >= 66 | |
| Tensile Strength, Yield | 30.23 MPa | 4384 psi | |
| Elongation at Yield | 500 % | 500 % | |
| 100% Modulus | 0.00340 GPa | 0.493 ksi | |
| 200% Modulus | 0.007598 GPa | 1.102 ksi | |
| 300% Modulus | 0.01290 GPa | 1.871 ksi | |
| Tear Strength | 40.8 kN/m | 233 pli | Die C |
| Compression Set | 33.4 % @Temperature 70.0 °C, Time 79200 sec | 33.4 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 8.00 min @Temperature 68.3 °C | 0.133 hour @Temperature 155 °F | |