- 拉伸强度 [MPa]: 28.19
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | >= 65 | >= 65 | |
| Tensile Strength, Yield | 28.19 MPa | 4089 psi | |
| Elongation at Yield | 504 % | 504 % | |
| 100% Modulus | 0.00300 GPa | 0.435 ksi | |
| 200% Modulus | 0.00660 GPa | 0.957 ksi | |
| 300% Modulus | 0.01140 GPa | 1.653 ksi | |
| Tear Strength | 37.3 kN/m | 213 pli | Die C |
| Compression Set | 33.7 % @Temperature 70.0 °C, Time 79200 sec | 33.7 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 12.5 min @Temperature 155 °C | 0.208 hour @Temperature 311 °F | |