- 拉伸强度 [MPa]: 32.19
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | >= 60 | >= 60 | |
| Tensile Strength, Yield | 32.19 MPa | 4669 psi | |
| Elongation at Yield | 586 % | 586 % | |
| 100% Modulus | 0.00250 GPa | 0.363 ksi | |
| 200% Modulus | 0.00560 GPa | 0.812 ksi | |
| 300% Modulus | 0.009901 GPa | 1.436 ksi | |
| Tear Strength | 32.0 kN/m | 183 pli | Die C |
| Compression Set | 39.7 % @Temperature 70.0 °C, Time 79200 sec | 39.7 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 12.0 min @Temperature 68.3 °C | 0.200 hour @Temperature 155 °F | |