- 拉伸强度 [MPa]: 27.7
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | >= 62 | >= 62 | |
| Tensile Strength, Yield | 27.70 MPa | 4017 psi | |
| Elongation at Yield | 621 % | 621 % | |
| 100% Modulus | 0.00220 GPa | 0.319 ksi | |
| 200% Modulus | 0.00450 GPa | 0.653 ksi | |
| 300% Modulus | 0.007901 GPa | 1.146 ksi | |
| Tear Strength | 39.7 kN/m | 227 pli | Die C |
| Compression Set | 36.4 % @Temperature 70.0 °C, Time 79200 sec | 36.4 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 12.5 min @Temperature 68.3 °C | 0.208 hour @Temperature 155 °F | |